304 stainless steel wire 304 stainless steel is a very common stainless steel, a density of 7.93 g / cm3, the industry also called 18/8 stainless steel. Its high-temperature metal products, processing performance, it is widely used in industrial and medical furniture industry and the food industry.
Common ground marking methods have 06Cr19Ni10, S30408, SUS304 three, including 06Cr19Ni10 generally expressed GB standard production, S30408 generally expressed ASTM standards, SUS 304 Japanese standard labeling standard.
304 is a versatile stainless steel, it is widely used to produce good overall performance requirements (corrosion resistance and formability) of equipment and parts. In order to maintain the inherent corrosion resistance of stainless steel, steel must contain more than 18% chromium, 8% nickel content above. 304 stainless steel is one of the United States in accordance with ASTM standard grades of stainless steel produced.
316 and 317 stainless steel (317 stainless steel performance, see below) is a stainless steel containing molybdenum species. 317 stainless steel, molybdenum content slightly clever in 316 stainless steel. Because molybdenum steel, the steel is superior overall performance 310 and 304 stainless steel, high temperature conditions, when the concentration of sulfuric acid is less than 15% and above 85%, the 316 stainless steel has a wide range of uses. 316 stainless steel also has good resistance to chloride corrosion performance, it is usually used in the marine environment. The maximum carbon content of 0.03 316L stainless steel can not be annealed for maximum corrosion resistance and require the use of welding. Carried out in the temperature range of 1850-2050 ° annealed, then rapidly annealed and then rapidly cooled. 316 stainless steel can be hardened thermal treatment. 316 stainless steel has good weldability. All standard welding methods may be used for welding. Welding according to use, respectively 316Cb, 316L stainless steel or 309Cb filler rods or rod welding. For optimum corrosion resistance, Stainless Steel Wire welding section 316 need to be annealed after welding. If you use Stainless Steel Fishing Wire , does not require annealing after welding.
Stainless steel wire, also known as stainless steel wire, stainless steel as raw material made of various types of different sizes and types of silk products, the origin of the United States, the Netherlands, Japan, the cross-section is generally round or flat. Common good corrosion resistance, high cost is 304 and 316 stainless steel wire stainless steel wire.
Stainless steel wires drawing (stainless steel wire rod drawing) under the action of the pulling force of the rod or wire drawing die blanks from the die orifice is pulled to the production of steel or non-ferrous metal wire small section of metal plastic processing. A variety of different cross-sectional shape and size of wire and metal alloys may be employed drawing production. Pull the wire, the precise size, smooth surface, and drawing equipment and tooling used in simple, easy to manufacture.
Process of drawing deformation index
Wire drawing process in increasing the length of the cross section is reduced, before drawing, after the wire cross-sectional area and length, respectively, F. , F and L. , L represents.
Stainless steel wire rope with a plurality of thin stainless steel wire or multi-strand twisted rope flexibility in material handling machinery for lifting, pulling, tensioning and load-bearing purposes. High strength 304 stainless steel wire rope, light weight, smooth, easy to suddenly break the whole root, reliable work.
Stainless steel wire rope use is:
1, non-direct high-speed, heavy load use.
The new stainless steel wire supplier rope not immediately in high-speed, heavy load directly, but to be a period of time at low speed, medium-load conditions, adapt to the use of the new state after the rope, wire rope and then gradually increase the speed and increase the lifting load.
2, is strictly prohibited quit.
Combined with the use of stainless steel wire rope pulley, it must be taken to prevent the rope from the wheel out of the slot. If the rope off the wheel groove after continued use, the rope will have kinks, broken wires, broken stocks, etc., prone to accidents.
3, non extrusion.
When using stainless steel wire rope can not be strongly pressed to avoid rope deformation, resulting in structural damage and broken wires appear early, or even broken rope off shares, significantly reduce the service life of the rope.
4, is strictly prohibited high-speed operation and other objects friction.
At high speeds, the wire rope and the instant when the frictional heat generated by the movement of objects to each other these may lead to emergence of martensite steel surface, which is the main reason for causing early wire breakage.
5. Do scattered wound.
When the stainless steel wire rope wrapped around the drum, should neatly as possible. If scattered wound, the rope at work due to squeezing each other will lead to destruction of the rope structure, resulting in an early broken wire, rope directly affect life.
6, prohibited the use of overload.
Stainless steel wire rope overload will increase its use by extrusion extent, the degree of wear and external wire round match between the grooves between the internal wire, shortening the life of the pulley.
7. Do a dramatic impact.
Several attacks can seriously shorten the life of the rope, the impact load overload the pit directly lead rope break.
8, in use should be done not wet.
Should be possible to use stainless steel wire in a dry environment. Easy to rust under the conditions of use of galvanized steel wire rope.